ASTM C + REDLINE: STANDARD SPECIFICATION FOR CONTACT- MOLDED REINFORCED THERMOSETTING PLASTIC (RTP) LAMINATES FOR. Start. Standard ASTM standard · ASTM C latest; Reinforced Plastic Piping Systems and Chemical Equipment; Plastic Building Products (ASTM VOL ) . C – 95 – This document is not an ASTM standard and is intended only to provide the user of an.
||7 September 2013
|PDF File Size:
|ePub File Size:
||Free* [*Free Regsitration Required]
The initial ply of the following lamination shall be 11? Consolidation of the composite laminate is by rolling.
This section of the laminate shall be allowed to exotherm prior to application of subsequent plies of reinforcement. In combination with the cured resin, the surfacing veil helps determine the thickness of the resin-rich layer, reduces microcracking, and provides a nonwicking chemically resistant layer.
The final ply shall be mat or chopped roving equivalent. Tensile modulus—1 psi MPa. Location of exotherm plies may be shifted within the laminate body.
This standard is issued under the fixed designation C ; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. E Test Method D The exterior surface shall also be fully cured.
Flexural modulus— psi MPa. C Corrosion barrier Plies 1, 2, and 3 shall gel before structural plies are added.
Lapped edges of adjacent layers shall be staggered. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. Consolidation of the composite laminate is by rolling.
C Cut edges must be covered with resin. D Corrosion barrier Plies 1, 2, and 3 shall gel before structural plies are added.
ASTM C582 – 09(2016)
This abstract is a brief summary of the referenced standard. Roll each ply for thorough wet-out and deaeration.
They are not arbitrarily selected values. B Calculated thickness for design purposes is determined as follows: Test Method D A surfacing mat is not required unless specified.
E Structural lay-up may be interrupted at intervals long enough to exotherm if required by the laminate manufacturing procedure and 6.
Parte 1 de 2 Standard Specification for Contact-Molded Reinforced Thermosetting Plastic C528 Laminates for Corrosion-Resistant Equipment1 C5582 standard is issued under the fixed designation C ; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision.
Astm c wilfredo row Enviado por: No plies may be omitted. D Foreign matter must not penetrate the surface and must not contribute to entrapped air or other defects not allowed. Pastes shall be made with thixotropic agents.
Astm c – astm normas fibra de vidrio
C Corrosion barrier Plies 1, 2, and 3 shall gel before structural plies are added. A superscript epsilon e indicates an editorial change since the last revision or reapproval. Astm a Astm a ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date. It is informational only and not an official part aetm the standard; the full text of the standard itself must be referred to for its use and application.
Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters.